SABIC Innovative Plastics LNP LUBRICOMP KA000 Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Aramid Fiber Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KA000 Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KA000 is a compound based on Acetal Copolymer resin containing Aramid Fiber, Proprietary Lubricant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.022 cm/cm | 0.014 - 0.022 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 8.8 % | 8.8 % | 5 mm/min; ISO 527 |
| Flexural Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Geon™ L6105 natural Polyvinyl Chloride, Rigid (PVC, Rigid)
- Plastcom SLOVAMID 6 T 20 PA6, 20% mineral filling
- Overview of materials for Phenolic, Novolac, Mineral Filled
- Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17510)
- JPJ Technologies PP PE35-1 Impact copolymer for Injection Molding
- LATI Latamid 12 H2 K/30 PA 12, 30% Carbon Fiber Reinforced, Heat Stabilized
- Teknor Apex Sinvicomp SIH 5009 Polyvinyl Chloride, Flexible
- LNP Lubricomp® PDX-J-91198 Polyethersulfone, Proprietary Filler (discontinued **)
- TIMET TIMETAL® 62S Titanium Alloy (Ti-6Al-2Fe-0.1Si); Alpha-Beta Forged, RA
Copyright © lookpolymers.com All Rights Reserved