SABIC Innovative Plastics LNP LUBRICOMP JX91198 PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP JX91198 PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* JX91198 is a compound based on Polyethersulfone resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.410 % | 0.410 % | 50% RH, 24 hrs; ASTM D570 |
| 0.530 % | 0.530 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16200 psi | ISO 527 |
| 116 MPa | 16800 psi | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D638 | |
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1 mm/min; ISO 527 |
| 10.13 GPa | 1469 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 161 MPa | 23400 psi | ISO 178 |
| 169 MPa | 24500 psi | ASTM D790 | |
| Flexural Modulus | 8.82 GPa | 1280 ksi | ASTM D790 |
| 9.23 GPa | 1340 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.31 J/cm | 6.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 8.06 x 10-8 mm³/N-M | 4.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX NX96302 PC+ABS
- PolyOne Geon™ 120 Series 124A Polyvinyl Chloride Homopolymer (PVC Homopolymer)
- Lubriplate FMO 150 AW USP Mineral Oil-Based Food Machinery Grade Oil
- Techmer ES Luriblend® PA6/6 GF43 ML2 BK 43% Glass Filled
- Tipco Tipcolite® TPF 1119 - Latex Modified Phenolic Resin having 26 mm Norton Flow with 9% Hexamine
- Tisan TISESTER® 30% Glass Fiber Reinforced, Flame Retardant (V0). Heat Stabilized. Polybutylene Terephthalate
- Arlon 56146R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Scotchcal™ ElectroCut™ 7125-14 Graphic Film
- Shin-Etsu Silicones SPD-Z6 Fluid
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 420, Hardened + 427°C Temper
Copyright © lookpolymers.com All Rights Reserved