Asahi Kasei Thermofil P-40TC-8100 40% Talc Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermofil |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermofil P-40TC-8100 40% Talc Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 46.9 MPa | 6800 psi | ASTM D790 |
| Flexural Modulus | 3.38 GPa | 490 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 µm/m-°C @Temperature 20.0 °C |
24.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C | 287 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.6 °C | 204 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in thickness |
| Flame Spread | 20 mm/min | 0.80 in/min | Horizontal Burn Rate; FMVSS302 |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckshield®-F 100 OPI 0.001" Diameter Wire, Allycarbonate EMI Shielding Window
- SABIC Innovative Plastics LNP LUBRICOMP DL003 PC
- Solvay Technyl® A 246M Nylon 66, Impact Grade, EH0
- Teknor Apex APEX® 92-A2292C-90 Polyvinyl Chloride, Flexible
- Dow Corning SZ-1180 Silicone Surfactant
- DuPont Performance Polymers Hytrel® 5555HS Polyester Elastomer TPC-ET (Unverified Data**)
- Chosun Refractories TG-68 Monolithic Refractories for Ladle and Tundish
- Braskem GM7746CA HDPE Blow Molding Polyethylene
- Braskem TI6800WV Impact Copolymer Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-326 (HS-HAF)
Copyright © lookpolymers.com All Rights Reserved