SABIC Innovative Plastics LNP LUBRICOMP DP0039EF PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DP0039EF PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DP0039EF is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.050 % | 0.050 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0068 cm/cm @Thickness 1.50 - 3.20 mm |
0.0068 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm @Thickness 1.50 - 3.20 mm |
0.0067 in/in @Thickness 0.0591 - 0.126 in |
SABIC Method |
| Melt Flow | 18.1 g/10 min @Load 2.16 kg, Temperature 300 °C |
18.1 g/10 min @Load 4.76 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | ISO 527 |
| 40.0 MPa | 5800 psi | ASTM D638 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| 50.0 MPa | 7250 psi | ISO 527 | |
| Elongation at Break | 14.7 % | 14.7 % | ASTM D638 |
| 17.5 % | 17.5 % | ISO 527 | |
| Elongation at Yield | 5.5 % | 5.5 % | ASTM D638 |
| 5.5 % | 5.5 % | ISO 527 | |
| Tensile Modulus | 2.09 GPa | 303 ksi | 1 mm/min; ISO 527 |
| 2.12 GPa | 307 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| 82.0 MPa | 11900 psi | ISO 178 | |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| 2.17 GPa | 315 ksi | ISO 178 | |
| Izod Impact, Notched | 3.02 J/cm | 5.66 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 20.0 J/cm | 37.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 129 kJ/m² | 61.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 23.0 J | 17.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 61.0 J | 45.0 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | ASTM D3702 Modified |
| K (wear) Factor | 850 x 10-8 mm³/N-M | 422 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 50 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion
- Polykemi AB POLYfill PPC T1030 Polypropylene Copolymer, Mineral Reinforced
- Rochling Engineered Plastics Polystone® XL Cross linked (UHMW-PE)
- Solvay TECHNYL® A 218 MZ15 V 25 PA66, 25/15% glass/mineral fiber, Conditioned
- Polyplastics Duranex® 7400F Polybutylene Terephthalate (PBT), Low friction, Low wear, 30% GF filled
- Arkema Group Orevac® 9307 Y Film EVA-MAH Terpolymer
- Advanced Ceramics ACL 2088 Zinc Alumino-Silicate
- Chesterton 652 Pneumatic Lubricant & Conditioner
Copyright © lookpolymers.com All Rights Reserved