SABIC Innovative Plastics LNP COLORCOMP M1000S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Colorcomp |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP COLORCOMP M1000S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0151 - 0.0167 cm/cm @Time 86400 sec |
0.0151 - 0.0167 in/in @Time 24.0 hour |
ISO 294 |
| 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0151 - 0.0167 cm/cm @Time 86400 sec |
0.0151 - 0.0167 in/in @Time 24.0 hour |
ISO 294 |
| 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ISO 527 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 40.0 MPa | 5800 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3780H TPE, PP Overmold or Standalone use
- Pau Tai UNISTAB EC-295 Stabilizers for Cable
- Huntsman PE1605 EVA Film Extrusion (discontinued **)
- Karina 811-10/23-A-ERYB-PO White PVC Compound
- Lucite International Lucite® 1192 Glass Separation Resin
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
- Dow Corning SYL-OFF® 7048 CROSSLINKER
- Arkema Group Rilsan® BMN Y TLD Nylon 11, MoS2 Filled (Dry)
- DSM Stanyl® TE350 Nylon 46 (European and Asian Grade) (Dry) (discontinued **)
- Radici Radilon® A 35E 990 (cond.) Nylon 66
Copyright © lookpolymers.com All Rights Reserved