Global EPP PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer Global EPP
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Global EPP PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PET is an unreinforced, semi-crystalline thermoplastic polyester, demonstrating dimensional stability similar to acetal, combined with the comparable wear resistance of nylon. Heavily loaded mechanical precision components subjected to sustained abrasive environments are particularly suited to this material.Key characteristics:Excellent dimensional stabilityHigh mechanical strength, hardness and rigidityExcellent wear resistanceGood creep resistanceLow moisture absorptionLow thermal expansionGood resistance to radiant energyGood electrical insulating propertiesStain resistantSuitable for food contactPET demonstrates outstanding dimensional stability, extremely low water absorption and relatively low thermal expansion. These properties are coupled to high mechanical strength, excellent creep and wear resistance, good electrical insulation and chemical resistance properties.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
Test Method A; ISO 1183:1987
Water Absorption 0.070 %

@Temperature 23.0 °C,
Time 86400 sec
0.070 %

@Temperature 73.4 °F,
Time 24.0 hour
Immersion; ISO 62:1999 (modified)
Moisture Absorption at Equilibrium 0.25 %
0.25 %
50% RH; ISO 62:1999
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62:1999
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
Sample Type 1B, 50mm/min; ISO 527-1/2:1993
Elongation at Break >= 15 %
>= 15 %
Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Modulus of Elasticity 3.70 GPa
537 ksi
Sample Type 1B, 50 mm/min; ISO 527-1/2:1993
Flexural Strength 100 MPa
14500 psi
1.5 mm/min; ISO 178:2001
Flexural Modulus 2.50 GPa
363 ksi
1.5 mm/min; ISO 178:2001
Compressive Strength 100 MPa
14500 psi
Sample Type B, 5 mm/min; ISO 604:2002
Compressive Modulus 2.80 GPa
406 ksi
Sample Type A, 1 mm/min; ISO 604:2002
Izod Impact, Notched (ISO) 2.00 kJ/m²
0.952 ft-lb/in²
Sample Type A; ISO 180:2000
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179-2:1999
Coefficient of Friction, Dynamic 0.25

@Pressure 1.75 MPa
0.25

@Pressure 254 psi
31.4 m/min
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-2:1999
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
ISO 8301:1991
Melting Point 255 °C
491 °F
Maximum Service Temperature, Air 110 °C
230 °F
Continuous
170 °C
338 °F
Intermittent
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75
Glass Transition Temp, Tg 70.0 °C
158 °F
ISO 11359-2:1999
Flammability, UL94 HB
HB
IEC 60695-11-10:2003-08
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093:1980-01
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093:1980-01
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250:1969-01
3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
IEC 60250:1969-01
Dielectric Strength 22.0 kV/mm
559 kV/in
IEC 60243-1:1998-01
Dissipation Factor 0.0010

@Frequency 100 Hz
0.0010

@Frequency 100 Hz
IEC 60250:1969-01
Comparative Tracking Index 600 V
600 V
IEC 60112:2003-01
Descriptive Properties Value Comments
Color White and Black