SABIC Innovative Plastics GELOY XP4034 ASA+PC

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY XP4034 ASA+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Available in a wide range of colors. Recommended for unpainted exterior/high heat/high impact applications.
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Water Absorption 0.25 %

@Time 86400 sec
 0.25 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 5.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 5.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
14 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 14 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
24 g/10 min

@Load 3.80 kg,
Temperature 280 °C
 24 g/10 min

@Load 8.38 lb,
Temperature 536 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 25 %
25 %
Type I, 50 mm/min; ASTM D638
126 %
126 %
50 mm/min; ISO 527
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 75.0 MPa
10900 psi
2 mm/min; ISO 178
88.0 MPa
12800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.51 GPa
364 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.20 J/cm
5.99 ft-lb/in
ASTM D256
0.800 J/cm

@Temperature -30.0 °C
 1.50 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 3.20 J/cm²
15.2 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 30.0 J

@Temperature -30.0 °C
 22.1 ft-lb

@Temperature -22.0 °F
 ASTM D3763
47.0 J

@Temperature 23.0 °C
 34.7 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -20.0 - 150 °C
 40.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -20.0 - 150 °C
 40.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
115 °C

@Thickness 3.20 mm
 239 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
104 °C

@Thickness 6.40 mm
 219 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 113 °C
235 °F
Rate B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 UL 94
Optical Properties Metric English Comments
Gloss 94 %
94 %
untextured, 60 degrees; ASTM D523
Descriptive Properties Value Comments
UV-light, water exposure/immersion F2
UL 746C