SABIC Innovative Plastics Cycoloy® XCM840 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® XCM840 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 260 °C |
10 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 12 g/10 min @Load 5.00 kg, Temperature 265 °C |
12 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 50 % | 50 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 5 mm/min; ASTM D638 |
| 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.00 GPa | 580 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*3; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Charpy Impact, Notched | 3.70 J/cm² | 17.6 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 60.0 J @Temperature 23.0 °C |
44.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 46.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 61.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 87554 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne Geon™ Vinyl Rigid Molding M5705 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Nye Lubricants 363F-UV (RL) Synthetic Oil
- PolyOne Edgetek® AS-30GF/000 BLACK Acrylonitrile Butadiene Styrene (ABS)
- Zircar Zirconia HfF-100 Hafnia Felt Insulation
- SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Europe-Africa-Middle East)
- SK Chemicals SKYTHANE® US518 Adhesive (Dry Lamination)
- Chengdu Polyster FH5550 Thermoplastic Polyether-ester Elastomer (TPEE)
- Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness)
- Axiall 19920 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved