SABIC Innovative Plastics Cycoloy® LG8002 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® LG8002 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive. Low gloss, high impact and ductility at 73F and -22F. UV-stable colors.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 260 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 5.87 J/cm @Temperature -30.0 °C |
11.0 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 6.40 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Impact Test | 40.0 J @Temperature -30.0 °C |
29.5 ft-lb @Temperature -22.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 47.0 J @Temperature 23.0 °C |
34.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C 177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 3.20 mm |
219 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 30 % | 30 % | untextured, 60 degrees; ASTM D 523 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR2-D-[color]-3 Polycarbonate, Improved Flame Retardant, Medium Flow, UV-stabilized
- Akro-Plastic Akromid® S31 (3484) PA 6.10 Conditioned (discontinued **)
- Hyosung Topilene R500S PP
- Kobe Steel KS-6-2-4-6 Alpha-Beta Titanium Alloy, AMS 4981, Solution treated and aged. Thickness ≤ 3 in.
- Karina 70900-35/1-E-AC Ivory PVC Compound
- Silberline Silvet® 410-30-E1
- UBE 1022MT2 Nylon 6 Monofilament (Drawing Ratio=5)
- Chosun Refractories SAL90Z Special High Alumina brick
- Braskem Idealis 500 High Molecular Weight Polyethylene Powder
- BASF Ultramid® A3W2G10 BK 20560 50% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved