SABIC Innovative Plastics Cycoloy® C8080REC PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C8080REC PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+ABS, Industrial quality resin with good flow, good temperature resistance and moderate ImpactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.43 %

@Temperature 23.0 °C
 0.43 %

@Temperature 73.4 °F
 ISO 62
Melt Flow 17 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 17 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
50 mm/min; ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527
Elongation at Break 50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 82.0 MPa
11900 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
20.0 kJ/m²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
50.0 kJ/m²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
51.0 kJ/m²

@Temperature 23.0 °C
 24.3 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
5.40 J/cm²

@Temperature 23.0 °C
 25.7 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 100 J
73.8 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 73.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 125 °C
257 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 128 °C
262 °F
Rate B/120; ISO 306
130 °C
266 °F
Rate B/50; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+16 ohm-cm
2.00e+16 ohm-cm
IEC 60093
Surface Resistance 4.40e+16 ohm
4.40e+16 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
 2.8

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 23.2 kV/mm

@Thickness 1.60 mm
 589 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
31.0 kV/mm

@Thickness 0.800 mm
 787 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 IEC 60250
0.018

@Frequency 50.0 - 60.0 Hz
 0.018

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C pass
IEC 60695-10-2