Skamol Group V-LITE 375 Vermiculite Insulating Brick
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Skamol Group |
| Trade Name | V-LITE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Skamol Group V-LITE 375 Vermiculite Insulating Brick.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
V-LITE vermiculite insulating bricks have the following characteristics: Max. service temperature 1100°C (2012°F)Hot-face applications and back-up insulationGood insulation valueHigh mechanical strengthHigh temperature resistance, withstand direct flame impingementCan be used in furnaces with reducing atmospheres due to their resistance to carbon monoxide and hydrocarbon attacksEqually suitable for hot-face applications and back-up insulation of refractory constructionsUsed for lining in all types of industrial kilns and furnaces, incinerators and combustion plantsInformation provided by Skamol.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.375 g/cc | 0.0135 lb/in³ | Dry |
| Loss On Ignition | 7.00 % @Temperature 1025 °C |
7.00 % @Temperature 1877 °F |
|
| Porosity | 86 % | 86 % | Total |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.000500 GPa | 0.0725 ksi | EN 993-6: 1995 |
| Compressive Strength | 1.30 MPa | 189 psi | EN 1094-5: 1995 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 750 °C |
6.11 µin/in-°F @Temperature 68.0 - 1380 °F |
BSÂ 1902: section 5.3: 1990 |
| Specific Heat Capacity | 0.940 J/g-°C | 0.225 BTU/lb-°F | |
| Thermal Conductivity | 0.120 W/m-K @Temperature 200 °C |
0.833 BTU-in/hr-ft²-°F @Temperature 392 °F |
Mean temp.; ASTMÂ C-182 |
| 0.140 W/m-K @Temperature 400 °C |
0.972 BTU-in/hr-ft²-°F @Temperature 752 °F |
ASTMÂ C-182 | |
| 0.160 W/m-K @Temperature 600 °C |
1.11 BTU-in/hr-ft²-°F @Temperature 1110 °F |
ASTMÂ C-182 | |
| Maximum Service Temperature, Air | 1100 °C | 2010 °F | |
| Shrinkage | 1.00 % @Temperature 1000 °C, Time 43200 sec |
1.00 % @Temperature 1830 °F, Time 12.0 hour |
Linear Reheat Shrinkage; EN 1094-6: 1999 |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 7.0 % | 7.0 % | |
| CaO | 2.0 % | 2.0 % | |
| Fe2O3 | 4.0 % | 4.0 % | |
| K2O | 11 % | 11 % | |
| MgO | 21 % | 21 % | |
| Na2O | 0.50 % | 0.50 % | |
| SiO2 | 47 % | 47 % | |
| TiO2 | 0.50 % | 0.50 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Light Brown | |
| Pyrometric Cone Equivalent | 1300°C | ASTM C24-89, ORTON cones |
| Resistance to Thermal Shock | Min 10 cycles | EN 993-11: 1998, heating to 950°C (1742°F) |
Users viewing this material also viewed the following:
- Haynes Hastelloy® alloy 188 12.7 mm plate weldments
- Master Bond MB297MED Cyanoacrylate Biocompatible Adhesive System
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- Master Bond EP3HT Fast Curing One Component Epoxy System
- Plastics Group Polifil® RMT-20 20% Talc-Reinforced Polypropylene, High Impact
- UBE UMERIT 1520F Metallocene LLDPE
- Cheng Yu Plastic T882GV1 Flame Retardant PBT, 10% Glass Fiber
- Domo Domamid® 33 Polyamide 6
- Arlon 51422R020 0.020" Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved