SABIC Innovative Plastics Cycolac® Z48 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® Z48 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive. Very high heat resistance with medium impact and good strength properties.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D 792 |
| Viscosity | 255000 cP @Temperature 260 °C |
255000 cP @Temperature 500 °F |
melt; 1000 sec-1; ASTM D 3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D 785 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 2.27 GPa | 329 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature -40.0 °C |
0.993 ft-lb/in @Temperature -40.0 °F |
ASTM D 256 |
| 2.13 J/cm @Temperature 23.0 °C |
3.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Gardner Impact | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 113 °C @Thickness 6.40 mm |
235 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 940ASR PC (Asia Pacific)
- Hexion Bakelite™ PF 31.9 Phenolic Formaldehyde Resin, Ammonia Free (discontinued **)
- Lanxess Durethan® AC 30 000000 Nylon 66
- Indium Corp. Indalloy 24 Bismuth Solder Alloy
- EMS-Griltech Griltex® D 1712A Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- BASF Ultraform® N2650 Z4 (LEV) POM
- Polykemi AB POLYelast TPE Z557 Thermoplastic Elastomer, SEBS-based
- SABIC Innovative Plastics LNP VERTON RX06424 PA 66
Copyright © lookpolymers.com All Rights Reserved