SABIC Innovative Plastics Cycolac® GHT3330 ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® GHT3330 ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat grade of ABS used for interior automotive components.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 16 % | 16 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.12 J/cm @Temperature 23.0 °C |
2.10 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 103 °C @Thickness 6.40 mm |
217 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Nylene® PA6 Glass Filled 5233 HS Nylon 6
- SABIC Innovative Plastics Lexan® PPC4504 PPC
- LG Chemical HIPS 460AF PS, Flame Retardant
- Materion Beryllium Nickel Strip - Alloy 360 Annealed, 2.5 hr at 950°F
- Indium Corp. In(OH)3 Crystalline Indium Hydroxide
- IRPC Polimaxx Polene 1100NN Polypropylene Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP HF008 PA 11 (Asia Pacific)
- Solvay ANTAROX® L 61 Surfactant
- A. Schulman POLYBATCH™ Red LL50304/3 Concentrate Based In LLDPE
- Abatron AboCast/AboCure 8110-3 Flexible Epoxy
Copyright © lookpolymers.com All Rights Reserved