Sichuan Deyang Haton® hGR302 PPS / F4 Polyphenylene Sulfide
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR302 PPS / F4 Polyphenylene Sulfide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, anti-frictionInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0026 cm/cm | 0.0026 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0078 cm/cm | 0.0078 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 106 | 106 | GB/T 3398.2-2008 |
| Tensile Strength | 159 MPa | 23100 psi | GB/T 1040.2-2006 |
| Elongation at Break | 2.0 % | 2.0 % | GB/T1040.2-2006 |
| Flexural Strength | 248 MPa | 36000 psi | GB/T 9341-2008 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 11.5 kJ/m² | 5.47 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m² | 20.5 ft-lb/in² | GB/T 1843-2008 |
| Coefficient of Friction | 0.25 | 0.25 | GB/T3960-1989 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 265 °C | 509 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.90e+16 ohm-cm | 1.90e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 2.30e+16 ohm | 2.30e+16 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-01 40% Glass Fiber Reinforced Polypropylene, Black
- Karina E 839-10/19-Y-CR White PVC Compound
- Multibase Multi-ABS 802 Utility Grade White
- Solvay Chemicals NOCOLOK® Flux P2 Potassium Fluoroaluminate
- Dow UNIPOL™ DGDA-5110 Polyolefin
- Axiall 1651 Clear 7002 Flexible PVC
- Braskem CP 741 Extrusion Polypropylene Heterophasic Copolymer
- PlastxWorld Veroplas PA2009L Nylon 6
Copyright © lookpolymers.com All Rights Reserved