Lehmann & Voss LUVOCOM® 1105-8000 PEEK, with carbon fiber, lubricant modified
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-8000 PEEK, with carbon fiber, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behaviour, self-lubricating, for highest tribologic needs.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 380 °C |
20 g/10 min @Load 22.0 lb, Temperature 716 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 170 MPa | 24700 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 15.0 GPa | 2180 ksi | |
| Flexural Strength | 235 MPa | 34100 psi | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Vicat Softening Point | 295 °C | 563 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm | |
| Insulation Resistance | >= 1.00e+9 ohm | >= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | graphite grey |
Users viewing this material also viewed the following:
- Micropol Microlin ML27 Linear Polyethylene Rotational Molding Powder
- Grupo Repol Dinalon® A1X25 V0 PA66, V0 red phosphorus and halogen free
- Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
- Menzolit Menzolit® BMC 2300 Unsaturated Polyester UP
- Saint-Gobain CHR® SG36-10(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- CeramTec Sonox® P508 Piezoceramic
- A. Schulman CP851 High Flow, Injection Molding Grade
- Polyram PlusTek RA325J5 Nylon 6.6, 25% Glass beads and Glass Fiber, Flame Retardant
- ExxonMobil 460 Mobil DTE FM Series
Copyright © lookpolymers.com All Rights Reserved