Rogers Corporation RT/duroid® 6035HTC Ceramic Filled PTFE Composite, High Power RF and Microwave

Category Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded
Manufacturer Rogers Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Rogers Corporation RT/duroid® 6035HTC Ceramic Filled PTFE Composite, High Power RF and Microwave.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features & Benefits:High thermal conductivity - Improved dielectric heat dissipation, enabling lower operating temperatures for high power applicationsLow loss tangent - Excellent high frequency performanceThermally stable low profile and reverse treated copper foil - Lower insertion loss and excellent thermal stability of tracesAdvanced filler system - Improved drillability and extended tools compared to alumina-containing circuit materialsLead-free process compatibleED and reverse treat copper foilApplications:High power RF and microwave amplifiersPower amplifiers, couplers, filters, combiners, power dividersInformation provided by Rogers Corporation.
Physical Properties Metric English Comments
Density 2.20 g/cc
0.0795 lb/in³
ASTM D792
Moisture Absorption at Equilibrium 0.060 %
0.060 %
D24/23; IPC-TM-650 2.6.2.1; ASTM D570
Thickness 254 - 1520 microns
10.0 - 60.0 mil
Range of Standard Thicknesses
Mechanical Properties Metric English Comments
Tensile Modulus 1.68 GPa
244 ksi
TD; 40 hours; 50%RH; ASTM D638
2.27 GPa
329 ksi
MD; 40 hours; 50%RH; ASTM D638
Peel Strength 1.38 kN/m

@Temperature 288 °C,
Time 20.0 sec
7.90 pli

@Temperature 550 °F,
Time 0.00556 hour
IPC-TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 19.0 µm/m-°C

@Temperature -55.0 - 288 °C
10.6 µin/in-°F

@Temperature -67.0 - 550 °F
X-, Y-Direction; ASTM D3386
39.0 µm/m-°C

@Temperature -55.0 - 288 °C
21.7 µin/in-°F

@Temperature -67.0 - 550 °F
Z-Direction; ASTM D3386
Thermal Conductivity 1.44 W/m-K

@Temperature 80.0 °C
9.99 BTU-in/hr-ft²-°F

@Temperature 176 °F
ASTM C518
Flammability, UL94 V-0
V-0
anticipated
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Condition A; Z direction; IPC 2.5.17.1
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Condition A; Z direction; IPC 2.5.17.1
Dielectric Constant 3.45 - 3.55

@Frequency 1.00e+10 Hz
3.45 - 3.55

@Frequency 1.00e+10 Hz
Z direction; Process; IPC-TM-650 2.5.5.5
3.6

@Frequency 8.00e+9 - 4.00e+10 Hz
3.6

@Frequency 8.00e+9 - 4.00e+10 Hz
Z direction; Design; Differential Phase Length Method
Dissipation Factor 0.0013

@Frequency 1.00e+10 Hz
0.0013

@Frequency 1.00e+10 Hz
Z direction; IPC-TM-650, 2.5.5.5
Descriptive Properties Value Comments
Dimensional Stability 0.07 mm/m
IPC-TM-650 2.4.3.8; X, Y direction; after etch, +E/150
0.07 mm/m
IPC-TM-650 2.4.3.9; X, Y direction; after etch, +E2/150
Thermal Coefficient of Dielectric Constant -66 ppm/°C
mod IPC-TM-650, 2.5.5.5; Z direction; -50°C to 150°C