Resinlab® SEC1233 Silver Filled Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Resinlab®
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Resinlab® SEC1233 Silver Filled Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resinlab™ SEC1233 is a silver filled, two component, room temperature curing epoxy adhesive. It is designed to cure completely at room temperature. SEC1233 provides excellent electrical conductivity useful in many electronic applications. It is a soft 100% solids thixotropic paste provided in a 1:1 ratio. It is recommended to mix by weight but extrusion of equal length beads from syringes is commonly used as a method of measurement as small quantities are commonly used. It also can be packaged in small side-by-side dispensing cartridges for use with static mixers. This system is also available in a pre-mix and frozen format. SEC1233 provides exceptionally high conductivity starting immediately after mixing and improves as the curing process proceeds. It also has the additional benefit of very high thermal conductivity due to its high silver loading. It gives good environmental protection while having tenacious adhesion to various metals and other common assembly materials.Information Provided by Resinlab L.L.C., an Ellsworth Adhesives Company.
Physical Properties Metric English Comments
Specific Gravity 3.90 g/cc
3.90 g/cc
Mixed; TM R050-16
Water Absorption <= 0.20 %

@Time 86400 sec
<= 0.20 %

@Time 24.0 hour
TM R050-35
Viscosity 29500 cP
29500 cP
10.0 rpm; TM R050-12
82250 cP
82250 cP
5.0 rpm; TM R050-12
172000 cP
172000 cP
Mixed, 2.5 rpm; TM R050-12
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
TM R050-17
Tensile Strength at Break 2.76 MPa
400 psi
TM R050-36
Tensile Strength, Ultimate 3.10 MPa
450 psi
TM R050-36
Tensile Strength, Yield 3.10 MPa
450 psi
TM R050-36
Elongation at Break 20 - 30 %
20 - 30 %
TM R050-36
Tensile Modulus 0.0689 GPa
10.0 ksi
TM R050-36
Compressive Yield Strength 13.8 MPa
2000 psi
TM R050-38
Compressive Strength 51.7 MPa
7500 psi
Break; TM R050-38
51.7 MPa
7500 psi
Ultimate; TM R050-38
Compressive Modulus 0.0758 GPa
11.0 ksi
TM R050-38
Adhesive Bond Strength 4.14 MPa
600 psi
Lap shear; 2024 T3 Al Abraded / MEK Wipe; TM R050-37
Thermal Properties Metric English Comments
CTE, linear 58.0 µm/m-°C

@Temperature <=40.0 °C
32.2 µin/in-°F

@Temperature <=104 °F
below Tg
120 µm/m-°C

@Temperature >=40.0 °C
66.7 µin/in-°F

@Temperature >=104 °F
above Tg
Thermal Conductivity 1.60 W/m-K
11.1 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air 150 °C
302 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Glass Transition Temp, Tg 40.0 °C
104 °F
TM R050-25
Electrical Properties Metric English Comments
Volume Resistivity 0.00030 ohm-cm
0.00030 ohm-cm
Cured: 1 hour at 60°C
0.00090 ohm-cm
0.00090 ohm-cm
Cured: 96 hours at 25°C
0.0016 ohm-cm
0.0016 ohm-cm
Cured: 24 hours at 25°C
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 60.0 °C
1.00 hour

@Temperature 140 °F
1440 - 4320 min

@Temperature 25.0 °C
24.0 - 72.0 hour

@Temperature 77.0 °F
Pot Life 60 min
60 min
Mass: 5g; TM R050-19
Descriptive Properties Value Comments
Color Silver