Reliance Industries Reclair F18010 Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | Reliance Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Reliance Industries Reclair F18010 Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Butene comonomer based Linear Low Density Polyethylene blow film grade. Applications:lamination films. Information provided by Reliance Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg |
0.90 g/10 min @Load 4.76 lb |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.5 MPa | 1810 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 10.3 g/micron | 262 g/mil | ASTM D1922 |
| Dart Drop | 3.50 g/micron | 88.9 g/mil | F<sub>50</sub>,38mm dart 66mm height; ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
Users viewing this material also viewed the following:
- Nilit FRIANYL C73 H-GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced
- Glastic SG-200 Corner Angles
- SABIC Innovative Plastics ULTEM 9075 PEI (Asia Pacific)
- Shakespeare WP-500 diameter 0.5 mm Hydrolytically Stabilized Polyester Yarn
- SABIC Innovative Plastics LNP THERMOCOMP ZX06323 PPE+HIPS (Asia Pacific)
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- A. Schulman POLYBATCH™ Brown 10305U Concentrate Based In LLDPE
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Black Peroxide Cure
- DuPont Teijin Films Mylar® EL Polyester Film, 142 Gauge
- Beijing Chemical Industry KAIFA® 301-G10F PBT Resin
Copyright © lookpolymers.com All Rights Reserved