Ravago Manufacturing Americas Hylex® P1010G7FRMA Polycarbonate, 7% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1010G7FRMA Polycarbonate, 7% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 7% Glass Filled, Flame RetardantInformation provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 3.100 GPa | 449.6 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 - 5VA @Thickness 3.00 mm |
V-0 - 5VA @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 20 PBT, 20% glass fibre
- Polimeri Europa Riblene® FF 20 Low Density Polyethylene - Blown Film Extrusion
- Pyrotek PROSILY G-10R Graphite Lubricant/Coating
- PolyOne Edgetek® PS-25MN/000 Polybutylene Terephthalate (PBT), Mineral Filled (discontinued **)
- NIZHNEKAMSKNEFTEKHIM PE 6949C (486H3) High Density Polyethylene
- SABIC Innovative Plastics LNP THERMOCOMP DF0089 PC
- ExxonMobil PP3295G1 Polypropylene Homopolymer
- Solvay TECHNYL® 1015CR PA6, Conditioned
Copyright © lookpolymers.com All Rights Reserved