Braskem EB861 Blown Film Extrusion Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem EB861 Blown Film Extrusion Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium-resistance films for general use; Mulching films; Shrink films; Coextrusion.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505/D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 240 % | 240 % | ASTM D882 |
| Film Elongation at Break, TD | 1090 % | 1090 % | ASTM D882 |
| Elmendorf Tear Strength TD | 100 g | 100 g | gF; ASTM D1922 |
| Dart Drop Test | 140 g | 0.309 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % @Thickness 0.0250 mm |
10 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 87 % @Thickness 0.0250 mm |
87 % @Thickness 0.000984 in |
60°; ASTM D2457 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics NORYL SA90 PPE
- Sibur NGP 30-32 Polyvinyl Chloride (PVC)
- Schwartz Technical Plastics OPTAMID® Cast Polyamide 6, Conditioned
- UBE UBEPOL BR34HL HIPS (stirring rate = 400 rpm)
- A. Schulman PP 3468-01 Polypropylene Homopolymer For High Speed Extrusion
- Trelleborg Emerson & Cuming Eccobond® C429-2 One-Component Silver Filled Electrically Conductive Epoxy Adhesive
- Denka VINYKON M1071 PVC, M grade for hard injection molding
- Overview of materials for Nylon 6, Unreinforced
- LNP Lubricomp® PDX-O-97635 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE Lubricant (discontinued **)&l
Copyright © lookpolymers.com All Rights Reserved