Radici Radilon® A USZ200 (dry) Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	Radici Group Plastics
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Radici Radilon® A USZ200 (dry) Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information provided by Radici group.

Physical Properties	Metric	English
Specific Gravity	1.04 g/cc	1.04 g/cc
Water Absorption	7.3 %	7.3 %
Moisture Absorption at Equilibrium	1.9 %	1.9 %

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	35.0 MPa	5080 psi
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	3.7 %	3.7 %
Tensile Modulus	16.5 GPa	2390 ksi
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F
Charpy Impact, Notched	7.50 J/cm² @Temperature -30.0 °C	35.7 ft-lb/in² @Temperature -22.0 °F
	8.50 J/cm² @Temperature 23.0 °C	40.4 ft-lb/in² @Temperature 73.4 °F

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F
Deflection Temperature at 0.46 MPa (66 psi)	140 °C	284 °F
Deflection Temperature at 1.8 MPa (264 psi)	65.0 °C	149 °F
Vicat Softening Point	180 °C @Load 5.10 kg	356 °F @Load 11.2 lb	50°C/h
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm