Quantum Acetal-Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum Acetal-Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Water Absorption at Saturation | 0.90 % | 0.90 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Hardness, Shore D | 85 | 85 | ASTM 2240 |
| Tensile Strength | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Compressive Strength | 103 MPa | 15000 psi | ASTM D695 |
| Compressive Modulus | 2.76 GPa | 400 ksi | ASTM D695 |
| Shear Strength | 55.2 MPa | 8000 psi | ASTM D732 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.15 | 0.15 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 97.2 µm/m-°C | 54.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.231 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 168 °C | 335 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | yes |
Users viewing this material also viewed the following:
- DuPont™ Clysar® LLP Polyolefin Shrink Packaging Film, 150 Gauge (discontinued **)
- Resinlab® CYNERGY CA6701 Adhesive
- Kingfa FRHIPS-702 Flame Retardant Polystyrene
- Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
- Techmer ES HiFill® PSU GF20 BK 20% Glass Filled
- Dow LIGHTER™ S93 Polyethylene Terephthalate (PET) Resin
- Arkema Group Lucalor® RY 123 CPVC, Plumbing Grade
- BASF Procom® C40H 458 Polypropylene
- Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM
Copyright © lookpolymers.com All Rights Reserved