Qualchem Danaprop PP2GF-15 Polypropylene, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Qualchem Zrt. |
| Trade Name | Danaprop |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Qualchem Danaprop PP2GF-15 Polypropylene, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polypropylene (homo-polymer) reinforced with glass fiberInformation provided by Qualchem Zrt.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 13 - 17 % | 13 - 17 % | |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238L |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Tensile Modulus | 3.78 GPa | 548 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | 10mm/min; ASTM D790 |
| Flexural Modulus | 3.15 GPa | 457 ksi | ASTM D790 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.24 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 159 °C | 318 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-THERM® 1646 Non-Insulating Interface Material
- Taiwan Sheen Soon Sheenthane® AH-782 TPU for Hotmelt Adhesive
- SABIC Innovative Plastics ULTEM 2310R PEI (Asia Pacific)
- Stir SpA Z 85 AT (PVC)
- Dow Corning SILASTIC® 9252/500P PARTS A&B
- 3M Scotchcal™ 8000-10 Graphic Film
- A. Schulman POLYBATCH™ Metallic Grey 80330/2
- Ineos H07D-00 Polypropylene Homopolymer
- ChevronTexaco Havoline® SAE 30 Motor Oil
Copyright © lookpolymers.com All Rights Reserved