- A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 3.31 GPa | 480 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® FF 25 Butene Copolymer Linear Low Density Polyethylene
- PolyOne Geon™ Vinyl Flexible R355AM Polyvinyl Chloride + NBR (PVC+NBR)
- Huntsman AVALON® 85 ABR Thermoplastic Polyurethane
- Freudenberg Simrit Superiorâ„¢ F815 Fluoroelastomer
- Styron CALIBREâ„¢ 301-15 Polycarbonate Resin
- Westlake Hifor LT74119 Linear Low Density Polyethylene
- ExxonMobil Escorene™ FL 00623 Ethylene Vinyl Acetate Copolymer (European Grade)
- Fainplast Compounds CRKA 91 Flexible PVC, Flame Retardant Electrical Bedding Lead Free
- Eagle Brass 1008 Low Carbon Steel, Full Hardened
- Arlon 30090R022 0.022" (0.559 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
Copyright © lookpolymers.com All Rights Reserved