Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer

Category	Polymer , Rapid Prototyping Polymer
Manufacturer	Proto3000
Trade Name	Objet Digital Materials™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Objet ABS-like Digital Material made of Object RGD515 & Objet RGD535Digital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide the desired mechanical properties and to resemble the product’s target materials.Information provided by Proto3000 for their protoyping engineering services.

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	67 - 69	67 - 69
Hardness, Shore D	85 - 87	85 - 87
Tensile Strength at Break	55.0 - 60.0 MPa	7980 - 8700 psi	ASTM D638-03
Elongation at Break	25 - 40 %	25 - 40 %	ASTM D638-05
Modulus of Elasticity	2.60 - 3.00 GPa	377 - 435 ksi	ASTM D638-04
Flexural Strength	65.0 - 75.0 MPa	9430 - 10900 psi	ASTM D790-03
Flexural Modulus	1.70 - 2.20 GPa	247 - 319 ksi	ASTM D790-04
Izod Impact, Notched	0.650 - 0.800 J/cm	1.22 - 1.50 ft-lb/in	ASTM D256-06

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	58.0 - 68.0 °C	136 - 154 °F	ASTM D648-06
	82.0 - 90.0 °C	180 - 194 °F	after thermal post treatment procedure A; ASTM D648-06
	92.0 - 95.0 °C	198 - 203 °F	after thermal post treatment procedure B; ASTM D648-06
Deflection Temperature at 1.8 MPa (264 psi)	51.0 - 55.0 °C	124 - 131 °F	ASTM D648-07
Glass Transition Temp, Tg	47.0 - 53.0 °C	117 - 127 °F	DMA, E