Premix Premi-Glas® 1200H-10 Fiberglass Reinforced Thermoset SMC

Category	Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset
Manufacturer	Premix
Trade Name	Premi-Glas®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Premi-Glas® 1200H-10 Fiberglass Reinforced Thermoset SMC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Premi-Glas® 1200H-10 is a fiberglass reinforced thermoset sheet molding compound for general purpose and HVAC applications requiring thermal stability and stiffness.Key features and benefits are:Good dimensional stability, including excellent thermal resistancePigmentable for molded-in color; best appearance with mold textureExcellent property retention in cold and hot environmentsSuitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1), see file E42524Designed for compression molding in matched metal die molds.Information provided by Premix.

Physical Properties	Metric	English	Comments
Specific Gravity	1.70 - 1.85 g/cc	1.70 - 1.85 g/cc
Linear Mold Shrinkage	0.0020 - 0.0035 cm/cm	0.0020 - 0.0035 in/in	Polymerization Shrinkage

Mechanical Properties	Metric	English	Comments
Tensile Strength	20.0 MPa	2900 psi	ASTM D638
Tensile Modulus	11.0 GPa	1600 ksi	ASTM D638
Flexural Strength	70.0 MPa	10200 psi	ASTM D790
Flexural Modulus	9.50 GPa	1380 ksi	ASTM D790
Compressive Strength	120 MPa	17400 psi	ASTM D695
Poissons Ratio	0.30	0.30
Shear Modulus	4.20 GPa	609 ksi	Calculated
Izod Impact, Notched	3.10 J/cm	5.81 ft-lb/in	ASTM D256
Izod Impact, Unnotched	3.65 J/cm	6.84 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C	19.4 µin/in-°F	Z Direction
CTE, linear, Transverse to Flow	25.0 µm/m-°C	13.9 µin/in-°F	XY Direction
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F
UL RTI, Electrical	130 °C	266 °F	UL 746C
UL RTI, Mechanical with Impact	130 °C	266 °F	UL 746C
UL RTI, Mechanical without Impact	130 °C	266 °F	UL 746C
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	15.0 kV/mm	381 kV/in	ASTM D149
Arc Resistance	180 sec	180 sec	ASTM D495

Processing Properties	Metric	English	Comments
Processing Temperature	150 °C	302 °F	Compression Molding
Clamp Pressure	3.45 - 6.89 MPa	500 - 1000 psi	Molding Pressure

Users viewing this material also viewed the following: