- Polyram RamTough RZ309G18 Polycarbonate, 18% Glass Fiber
Polyram RamTough RZ309G18 Polycarbonate, 18% Glass Fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough RZ309G18 Polycarbonate, 18% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
18% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | DIN 53479 |
| Water Absorption | 0.29 % | 0.29 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM-D790 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.950 J/cm @Temperature 23.0 °C |
1.78 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | DIN 53461 |
| Flammability, UL94 | V-1 @Thickness 3.00 mm |
V-1 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9950C TPE, ABS/PC Overmold
- Polimeri Europa Clearflex® FG 336 Hexene Copolymer Linear Low Density Polyethylene
- Nilit FRIANYL B63 L-HS-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- Victrex® PEEK 150CA30 30% Carbon Fiber Reinforced
- Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled
- Seals Eastern 7130 Fluorocarbon-Elastomer
- Chase Plastics CP Pryme® N110L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated
- A. Schulman POLYBATCH™ Blue LL40445/2 Concentrate Based In LLDPE
- A. Schulman POLYBATCH™ Yellow P20199/2 Concentrate Based In Copolymer PP
- Fainplast Compounds PH 75/AS Flexible PVC, Transparent Extrusion
Copyright © lookpolymers.com All Rights Reserved