Polyram RamTal RM2309 Acetal, Injection Molding
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal RM2309 Acetal, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Acetal copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 60.0 MPa | >= 8700 psi | ASTM-D638 |
| Elongation at Break | >= 30 % | >= 30 % | ASTM-D638 |
| Flexural Strength | >= 75.0 MPa | >= 10900 psi | ASTM-D790 |
| Flexural Modulus | >= 2.50 GPa | >= 363 ksi | ASTM-D790 |
| Izod Impact, Notched | >= 0.600 J/cm @Temperature 23.0 °C |
>= 1.12 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | DIN 53461 |
| Vicat Softening Point | 150 °C | 302 °F | ASTM-D1525 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Rogers Corporation RO4535 Ceramic-Filled, Glass-Reinforced Hydrocarbon Laminate
- NOVA Chemicals Surpass® RMs539-UG Octene sMDPE Rotational Molding Film
- Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 7781 E-Glass Reinforced
- SABIC Innovative Plastics Lexan® DMX6014 PC Copolymer (Asia Pacific)
- MetalTek Nitronic® 50 Cast UNS J93790 Austenitic Stainless Steel
- Teknor Apex HFFR 2003PC Polyolefin, Halogen Free
- Teknor Apex Monprene® MP-1500L2 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Blue 4656 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ Yellow LL20203/2 Concentrate Based In LDPE
- Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Conditioned (2.5% Moisture)
Copyright © lookpolymers.com All Rights Reserved