Polyram RamTal PM7013G2 Acetal, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM7013G2 Acetal, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber reinforced and UV stabilized polyacetal for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | DIN 53479 |
| Water Absorption | 0.20 % | 0.20 % | DIN 53495 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM-D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced
- Solvay Engineered Polymers SEQUEL® 1493 Engineered Polyolefin (discontinued **)
- Covestro Bayblend® KU 2-1473 Polycarbonate/ABS Blend (discontinued **)
- 3M Dyneon™ TFM™ 1705 Modified PTFE Powder (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8048 PEEK, with carbon fiber
- Sibur Nitrilast-33 Nitrile-Butadiene Rubber (NBR)
- Shin-Etsu Silicones KE-5540U Low Temperature Silicone Elastomer
- Arkema Group Orgalloy® RS 6000 Nylon 6 Alloy, Rigid Grade (Conditioned)
- SABIC Innovative Plastics NORYL PX2355 PPE+HIPS (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved