Polyram RamOfin PPC500 Polypropylene, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC500 Polypropylene, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM-D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM-D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM-D790 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature 23.0 °C |
1.87 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Proto3000 CastForm™ PS Selective Laser Sintering (SLS®) Prototyping Polymer
- Lehmann & Voss LUVOCOM® 80-8284 Polyacetal-copolymer, with carbon fiber
- Mateck LiGaO2
- Lanxess Durethan® BKV 130 H2.0 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified
- SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10
- Teknor Apex Sinpolene MBB1512 Low Density Polyethylene
- DSM Akulon® S223-HM8 (Dry) 40% Mineral Reinforced, Heat Stabilized Nylon 66 (North America)
- CP-Polymer-Technik Wellamid® 6000 MR 209 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
- Fainplast Compounds GS 59/C Flexible PVC, Injection Molding for Footwear
- BASF Ultramid® B36 LN 01 PA6
Copyright © lookpolymers.com All Rights Reserved