Polyram RamOfin PPC343T4 Polypropylene, 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC343T4 Polypropylene, 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Mineral filled, UV stabilized, heat stabilized polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 75 % | 75 % | ISO 527 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 168 °C | 334 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75 |
| Vicat Softening Point | 155 °C | 311 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 22.1 mm/min | 0.870 in/min | FMVSS302 |
Users viewing this material also viewed the following:
- Nye Lubricants 300 (SO) Synthetic Oil
- SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer (Asia Pacific)
- Chevron Phillips LX8119 HDPE Injection Molding Resin (discontinued **)
- Chevron Phillips K-Resin® BK12 Styrene-Butadiene Copolymer, Injection Molding Grade (discontinued **)
- Freudenberg Simrit V141 Standard Fluoroelastomer
- Gromax PBT 1100-211M
- Möller Medical PolySkin 102 M NanoCoating
- Solvay Specialty Polymers Hylar® 5000 HG Polyvinylidene Fluoride (PVDF)
- SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific)
- PolyOne Synprene® RT-3630 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved