Dow DOWLEX™ 2045.11 Linear Low Density Polyethylene, Heavy Duty Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2045.11 Linear Low Density Polyethylene, Heavy Duty Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOWLEX® 2045.11 Polyethylene resin is a premier film resin for general purpose packaging applications, ranging from heavy duty applications to high speed, thin gauge applications. It contains high level of slip additive and medium level of antiblock additive, and offers additional thermal stability. This resin complies with U.S. FDA regulation 21 CFR 177.1520 (c) 3.2 (a) for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg |
1.0 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | |
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 520 % | 520 % | |
| Film Elongation at Break, TD | 670 % | 670 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Elmendorf Tear Strength MD | 260 g | 260 g | |
| Elmendorf Tear Strength TD | 640 g | 640 g | |
| Elmendorf Tear Strength, MD | 10.4 g/micron | 264 g/mil | |
| Elmendorf Tear Strength, TD | 25.6 g/micron | 650 g/mil | |
| Dart Drop | 8.40 g/micron | 213 g/mil | |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | |
| Film Tensile Strength at Break, TD | 37.2 MPa | 5400 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 106 °C | 223 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 10 % | 10 % | |
| Gloss | 55 % | 55 % | 45° |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 226 °C | 439 °F | Film extrusion temperature |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 BT B 27 A/IM PA66
- Nilit FRIANYL A63 GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced
- Polykemi AB POLYshine PBT D223 GF20 FR PBT, Glass-Fiber Reinforced, Flame Retardant
- Ineos ABS Centrex® 815 ASA Blend (discontinued **)
- Karina E 500D08/201 Beige PVC Compound
- Solvay Specialty Polymers Ryton® R-4-240BL Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Saint-Gobain CHR® 2302-5R UHMW Film Backing Acrylic Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved