Polyram RamLloy PN300G4 PPE/PS Alloy, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamLloy PN300G4 PPE/PS Alloy, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE/PS alloy, 20% glass fiber reinforced for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.0060 % | 0.0060 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 2577 |
| Melt Flow | 12 g/10 min @Load 10.0 kg, Temperature 280 °C |
12 g/10 min @Load 22.0 lb, Temperature 536 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Dow Isoplast® 202 Polyurethane (PUR-RT), Impact Modified (discontinued **)
- Gromax BPR20-N1 Nylon 6, Flame Retardant (Conditioned)
- Taiwan PU Corporation TPU-C75 General Grade, Calender Molding Polyester Base TPU
- Samsung Cheil Industries Starex® VH-0810 ABS, Unreinforced FR
- Techmer ES HiFill FR® PA6 GF13 FR-N BK 13% Glass Filled
- Borealis Daplen™ KB4436 Polypropylene TPO Compound
- A. Schulman FORMION™ FI 330 Ionomer
- Eastman Eastar EN001 Copolyester
- Arkema Group Cristamid® MS 1700 Semi-Aromatic Nylon (PASA) (Conditioned)
- ExxonMobil Escorene® HD-8661 LHDPE Rotational Molding Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved