Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDPE 2004TC37: Light duty film used for very thin films requiring good optical properties for general packaging.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 4.7 g/10 min | 4.7 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO R527-1 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO R527-1 |
| Elongation at Break | 100 % | 100 % | ISO 527, MD |
| >= 450 % | >= 450 % | ISO 527, TD | |
| Modulus of Elasticity | 0.190 GPa | 27.6 ksi | TD; ISO R527-1 |
| 0.190 GPa | 27.6 ksi | MD; ISO R527-1 | |
| Tensile Impact | 150 J/cm | 281 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
| 80.0 kN/m | 456 pli | MD; ISO 6383-2 | |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO R527-1 |
| Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ISO R527-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.5 % | 9.5 % | ASTM D1003A |
| Gloss | 53 % | 53 % | ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clarity, mV | 23 | Sabtec |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® RCM6134 PC+ABS (Asia Pacific)
- Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound
- Ineos H35Z-GP Polypropylene Homopolymer
- Greene Tweed CHEMRAZ® 550 Perfluoroelastomer
- SABIC Innovative Plastics Valox® VX8015U PBT+PET (Europe-Africa-Middle East)
- Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg IM2-C Fibre
- 3M 9498 Splicing Tape
- Eastman Tenite Butyrate 465E3720008 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
- BASF Styropor® P 240 EPS
Copyright © lookpolymers.com All Rights Reserved