Polyram Polytron P30B03 Copolymer Polypropylene, Chemically Coupled 30% Long Glass Fiber

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Polyram
Trade Name Polytron
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polyram Polytron P30B03 Copolymer Polypropylene, Chemically Coupled 30% Long Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A CHEMICALLY COUPLED 30% LONG GLASS FIBERS REINFORCED BLACK POLYPROPYLENE, HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.These products have significantly improved impact performance characteristics compared to other grades of Polypropylene long fiber thermoplastics. The room temperature Charpy impact properties are 25 to 30% higher at room temperature and at low temperature (-40 C). Information provided by Polyram Ram On Ind.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM-D792
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.0 MPa
12300 psi
ASTM-D638
Elongation at Break 2.9 %
2.9 %
ASTM-D638
Tensile Modulus 5.50 GPa
798 ksi
ASTM-D790
Flexural Strength 140 MPa
20300 psi
ASTM-D790
Flexural Modulus 5.30 GPa
769 ksi
ASTM-D790
Izod Impact, Notched 1.70 J/cm

@Temperature 23.0 °C
3.18 ft-lb/in

@Temperature 73.4 °F
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 149 °C
300 °F
ASTM-D648
Flammability, UL94 HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Flame Spread 10 mm/min
0.39 in/min
FMVSS302