Polyram PlusTek PB845 Nylon 6 for Injection Molding, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB845 Nylon 6 for Injection Molding, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified Nylon 6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.012 - 0.016 cm/cm | 0.012 - 0.016 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 55 % | 55 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 2.11 GPa | 306 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous use |
| 180 °C | 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 10 mm/min | 0.39 in/min | FMVSS302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- SABIC 318CN Linear Low Density Polyethylene for Wire & Cable
- Microtherm Group Slim&Light Fire Resistant Insulation
- Momentive Performance Materials RTV5242 White Adhesive Sealant, Fast Cure Paste
- Lucky IF-870 Acrylic, High Flow Grade
- SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66
- Solvay JAGUAR® EXCEL Surfactant
- Tipco Tipcolene® HR 8234 - 10% Talc/Mineral Reinforced Polypropylene Copolymer, Very High Impact Strength & Flow
- Dow INTEGRAL™ 932 High Heat Multilayer Adhesive Film
- Alloy Wire International RW 122 Hot Cutting Wire - High Strength
- Buckeye Polymers BP RPP 2012 TR BLK Polypropylene, Talc Filled
Copyright © lookpolymers.com All Rights Reserved