Polyram PA500 Nylon 6.6, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PA500 Nylon 6.6, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | DIN 53479 |
| Water Absorption | 7.0 % | 7.0 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0090 - 0.016 cm/cm | 0.0090 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM-D785 |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM-D638 |
| Elongation at Break | 20 % | 20 % | ASTM-D638 |
| Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 100 °C | 212 °F | Continuous Use |
| >= 180 °C | >= 356 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CH120 Polypropylene, Homopolymer, Injection Molding, Barefoot
- DuPont™ Sclairfilm® LX-1 LLDPE Film, Laminating, 76.2 µm Thickness (discontinued **)
- Ineos ABS Lustran® SAN GF20 Glass Fiber Reinforced
- Momentive Performance Materials Silpruf® Construction Sealant
- Indorama Auriga Polymers Polyclearâ„¢ Perserve 2201 PET Resin
- 3M 4318 Foam Tape
- Cheng Yu Plastic FV30G25 POM, 25% Glass Fiber
- Overview of materials for Ionomer, Film Grade
Copyright © lookpolymers.com All Rights Reserved