Polykemi AB SCANTEC PC S75R GF10 V0 Polycarbonate, Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | SCANTEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANTEC PC S75R GF10 V0 Polycarbonate, Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | With Flow; ISO 2577 |
| 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 45.0 MPa | <= 6530 psi | ISO/R527 |
| Elongation at Break | 7.0 % | 7.0 % | ISO/R527 |
| Flexural Strength | <= 120 MPa | <= 17400 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa @Temperature 23.0 °C |
508 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| 0.700 J/cm² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 143 °C @Load 5.001 kg |
289 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- SCG Chemicals EL-Leneâ„¢ M3204 Butene (C4) Rotational Molding Resin
- Teknor Apex Monprene® MP-2760 Thermoplastic Elastomer
- Universal Wire Works Rene 41 (AMS 5800) Filler Metal
- DuPont™ Bynel® 41E865 Anhydride Modified LLDPE
- Barlog Plastics KEBAFORM C 909 WR POM Copolymer unreinforced, UV-stabilized
- BASF Formic Acid - 90%
- 3M ScotchPad™ 832CP Pouch Tape Pads
- PlastiComp Complet® LCF50 - PA66 MT Nylon 66, 50% Long Carbon Fiber Reinforced, Impact Modified
- Beijing Ranger Chem HY-127 Liquid Epoxy Resin
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 90A, Non-Black Peroxide Cure
Copyright © lookpolymers.com All Rights Reserved