ExxonMobil PP7011L1 Polypropylene Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil PP7011L1 Polypropylene Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: An impact copolymer resin for extrusion applications with high melt viscosity and excellent low-temperature impact strength. It is suitable for cables, pipes, profiles, sheets and thermoforming.Availability: Africa & Middle East and Europe Features:High Impact Resistance Low Flow Uses: CompoundingCorrugated PipeElectrical/Electronic ApplicationsIndustrial ApplicationsProcessing Method: Extrusion, Extrusion Blow Molding, Injection Molding, Profile Extrusion, Sheet Extrusion and ThermoformingAutomotive Specifications: Daimler Chrysler DBL 5404Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ExxonMobil Method
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 230 °C	1.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
	4.0 g/10 min @Load 5.00 kg, Temperature 230 °C	4.0 g/10 min @Load 11.0 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	ISO 868
Tensile Strength, Yield	26.0 MPa	3770 psi	ISO 527-2/50
Elongation at Yield	10 %	10 %	ISO 527-2/50
Tensile Modulus	1.10 GPa	160 ksi	Secant; ISO527-2/1
Flexural Modulus	1.15 GPa	167 ksi	Secant; ISO 178
Izod Impact, Notched (ISO)	35.7 kJ/m²	17.0 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.441 J/cm² @Temperature -20.0 °C	2.10 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.609 J/cm² @Temperature 0.000 °C	2.90 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eA
	3.36 J/cm² @Temperature 22.8 °C	16.0 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	322 °C	612 °F	ISO 3146
Crystallization Temperature	234 °C	453 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	82.8 °C	181 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ISO 75-2/A
Vicat Softening Point	149 °C	300 °F	ISO 306/A50