Polykemi AB SCANMID 6 B12^ F30 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B12^ F30 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.0090 cm/cm
0.0090 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 80

@Time 15.0 sec
 80

@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 170 MPa
<= 24700 psi
ISO/R527
Elongation at Break 3.0 %
3.0 %
ISO/R527
Flexural Strength <= 240 MPa
<= 34800 psi
ISO 178
Flexural Modulus 8.80 GPa

@Temperature 23.0 °C
 1280 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.800 J/cm²

@Temperature -20.0 °C
 3.81 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 200 °C

@Load 5.001 kg
 >= 392 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1