GEHR Plastics ECOGEHRÂ® PA 6.10 Nylon 6.10 Dry, 60% Sebacic Acid

Category	Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer	GEHR Plastics Inc
Trade Name	ECOGEHR®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	GEHR Plastics ECOGEHRÂ® PA 6.10 Nylon 6.10 Dry, 60% Sebacic Acid.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Nylon 6.10 is 60 % sebacic acid, which is obtained from castor oil. This material combines a low density (for polyamide) with good cold impact strength, and its low water absorption makes it very dimensionally stable. This is in addition to a very high (for bio-based polymers) continuous usage temperature of 212Â°F and its chemical resistance to organic solvents, for which PA is well known. This material can thus be used not only in traditional Nylon 6 applications, but also where the use of Nylon 6 previously reached its limits.Information provided by GEHR Plastics, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.08 g/cc	1.08 g/cc	ASTM D792
Water Absorption	1.4 %	1.4 %	ASTM D570

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	69.98 MPa	10150 psi	ASTM D638
Elongation at Yield	4.5 %	4.5 %
Modulus of Elasticity	2.50 GPa	362 ksi	ASTM D638
Izod Impact, Notched (ISO)	44.1 kJ/mÂ²	21.0 ft-lb/inÂ²	ASTM D256
Izod Impact, Unnotched (ISO)	NB	NB	ASTM D256

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	100 Â°C	212 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	65.0 Â°C	149 Â°F	HDT/A; ASTM D648

Descriptive Properties	Value	Comments
Industrially Biodegradable	No
Renewable Content (%)	63