- Polykemi AB POLYfill PPH GF5020 PD1 VT2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled, Heat Stabilized
Polykemi AB POLYfill PPH GF5020 PD1 VT2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Polykemi AB |
| Trade Name | POLYfill |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Polykemi AB POLYfill PPH GF5020 PD1 VT2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | With Flow; ISO 2577 |
| 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 5.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
5.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 70.0 MPa | <= 10200 psi | ISO/R527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO/R527 |
| Flexural Strength | <= 100 MPa | <= 14500 psi | ISO 178 |
| Flexural Modulus | 3.80 GPa <br>@Temperature 23.0 °C |
551 ksi <br>@Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.450 J/cm² <br>@Temperature -20.0 °C |
2.14 ft-lb/in² <br>@Temperature -4.00 °F |
ISO 179 |
| 0.600 J/cm² <br>@Temperature 23.0 °C |
2.86 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 115 °C <br>@Load 5.001 kg |
239 °F <br>@Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
|
| Glow Wire Test | 750 °C <br>@Thickness 2.00 mm |
1380 °F <br>@Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® F-562 Phenolic Prepreg, C2 Carbonized Rayon Reinforced
- Sylvin Technologies 8940-90 Natural PVC Extrusion Compound
- Shakespeare NX-203 diameter 0.2 mm Nylon 6 Monofilament
- SABIC Innovative Plastics LNP THERMOCOMP UX93847 PPA (Asia Pacific)
- Toyobo GLAMIDE® T-663G50 Nylon-66
- EMS-Griltech Grilon® BN 20R Nylon 6 Monofilament (Non-Set)
- ExxonMobil Exceed™ 1012 MK Metallocene Polyethylene Resin
- ATI Allegheny Ludlum AL 433™ Ferritic Stainless Steel, Annealed
- AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M
- Zhejiang Juner PC-A1-18 Top-Grade Flame Retardant UV-Resistant
Copyright © lookpolymers.com All Rights Reserved