Aremco Ceramabond™ 865 High Temperature Ceramic Adhesive/Paste, Aluminum Nitride Filled

Category	Ceramic , Nitride
Manufacturer	Aremco
Trade Name	Ceramabond™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aremco Ceramabond™ 865 High Temperature Ceramic Adhesive/Paste, Aluminum Nitride Filled.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Thermal Conductivity Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Probes, Sensors

Physical Properties	Metric	English	Comments
Density	1.95 - 2.15 g/cc	0.0704 - 0.0777 lb/in³
Volatile Organic Compounds (VOC) Content	0.000 g/l	0.000 g/l

Mechanical Properties	Metric	English	Comments
Impact Test	36.6 J	27.0 ft-lb	Torque Strength; curing at 1000°F

Thermal Properties	Metric	English	Comments
CTE, linear	2.70 µm/m-°C	1.50 µin/in-°F
Maximum Service Temperature, Air	1650 °C	3000 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	7.36 kV/mm	187 kV/in

Processing Properties	Metric	English	Comments
Processing Temperature	50.0 - 90.0 °C	122 - 194 °F	Application Temp
Cure Time	120 min @Temperature 93.3 °C	2.00 hour @Temperature 200 °F	Step 1, preceeded by 1-4 hour air set
	120 min @Temperature 177 °C	2.00 hour @Temperature 350 °F	Step 2
	120 min @Temperature 260 °C	2.00 hour @Temperature 500 °F	Step 3
Shelf Life	6.00 Month @Temperature 4.44 - 32.2 °C	6.00 Month @Temperature 40.0 - 90.0 °F

Descriptive Properties	Value	Comments
Acid Resistance	Good	after curing at 700°F for 2 hours
Alkali Resistance	Good	after curing at 700°F for 2 hours
Color	Gray
Moisture Resistance	Excellent	after curing at 700°F for 2 hours
Solvent	Water
Thinner	865-T