PolyOne Trilliant™ HC HC3220-0030 RS Natural Polycarbonate (PC)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	PolyOne Corporation
Trade Name	Trilliant™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Trilliant™ HC HC3220-0030 RS Natural Polycarbonate (PC).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead of the competition. When specified, Trilliant® compounds may incorporate agency rated materials that meet USP Class VI, FDA or ISO 10993 testing requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.41 g/cc	1.41 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	117 MPa	17000 psi	Type I, 51 mm/min; ASTM D638
Elongation at Break	9.0 %	9.0 %	Type I, 51 mm/min; ASTM D638
Flexural Strength	186 MPa	27000 psi	ASTM D790
Flexural Modulus	7.24 GPa	1050 ksi	ASTM D790
Izod Impact, Notched	1.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.25 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Melting Point	288 - 310 °C	550 - 590 °F
Deflection Temperature at 0.46 MPa (66 psi)	>= 143 °C @Thickness 3.18 mm	>= 289 °F @Thickness 0.125 in	Annealed; ASTM D648

Processing Properties	Metric	English
Mold Temperature	65.6 - 76.7 °C	150 - 170 °F
Drying Temperature	93.3 °C	200 °F
Dry Time	3.00 hour	3.00 hour

Descriptive Properties	Value	Comments
Agency Ratings	USP Class VI
Appearance	Natural Color
Features	Biocompatible
	Good Chemical Resistance
	Good Colorability
	Good Impact Resistance
	Specialty Grade
Filler / Reinforcement	Glass Fiber Reinforcement, 30% Filler by Weight
Forms	Pellets
Generic Material	PC
Generic Name	Polycarbonate (PC)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Hospital Goods
	Housings
	Medical Appliances
	Medical/Healthcare Applications