Abatron AboCast 50-11/AboCure 50-17 Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy
Manufacturer	Abatron
Trade Name	AboCast
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 50-11/AboCure 50-17 Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Information provided by Abatron, Inc.Processing: Shelf life: 12+ months (unmixed). 100/27 ratio. Pot life: 500 g, 29 min. at 70°C (160°F). Exothermic Peak 270°C (520°F). Cures in 1-2 hrs at 80-100°C (175-212°F) + 1-3 hrs at 120-160°C (250-320°F). For large castings: 8-24 hrs at RT until hard + 1-2 hrs at 80°C (175°F) + 1-2 hrs at 100°C (212°F) + 1-2 hrs at 120°C (250°F) + (optional) 1-2 hrs at 150-160°C (300-355°F). Do not demold before 100°C cure cycle.

Physical Properties	Metric	English	Comments
Viscosity Measurement	100 @Temperature 70.0 °C	100 @Temperature 158 °F

Mechanical Properties	Metric	English
Hardness, Rockwell M	101	101
Tensile Strength, Ultimate	78.46 MPa	11380 psi
Elongation at Break	8.5 %	8.5 %
Flexural Yield Strength	112.7 MPa	16350 psi
Flexural Modulus	2.48 GPa	360 ksi
Compressive Yield Strength	107.6 MPa	15610 psi
Compressive Modulus	1.87 GPa	271 ksi
Izod Impact, Notched	0.240 J/cm	0.450 ft-lb/in

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	123 °C	253 °F	Deflection temperature; load unknown.

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.24e+16 ohm-cm	>= 1.24e+16 ohm-cm
Surface Resistance	3.53e+15 ohm	3.53e+15 ohm
Dielectric Constant	3.55 @Frequency 1e+6 Hz	3.55 @Frequency 1e+6 Hz
	4.01 @Frequency 1000 Hz	4.01 @Frequency 1000 Hz
	4.06 @Frequency 60 Hz	4.06 @Frequency 60 Hz
Dissipation Factor	0.0047 @Frequency 60 Hz	0.0047 @Frequency 60 Hz
	0.012 @Frequency 1000 Hz	0.012 @Frequency 1000 Hz
	0.037 @Frequency 1e+6 Hz	0.037 @Frequency 1e+6 Hz

Processing Properties	Metric	English	Comments
Pot Life	29.0 min @Temperature 70.0 °C	29.0 min @Temperature 158 °F	500 g

Descriptive Properties	Value	Comments
Exotherm	270°C	Peak