PolyOne Therma-Tech™ SF-5000C TC Polyphenylene Sulfide (PPS) (discontinued **)

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Therma-Tech™ SF-5000C TC Polyphenylene Sulfide (PPS) (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of thermoplastics. These materials provide the benefits of proprietary conductive additive technologies and the performance of select engineering thermoplastic resins. Therma-Tech compounds have been shown to improve thermal conductivity up to 100-times that of conventional plastics and can be used in a wide range of thermal management applications.Description/Features:PPS (Polyphenylenesulfide)Thermally ConductiveElectrically InsulativeApplications: EnclosuresHeat SinksMotor componentsProcessing Method: Injection MoldingInformation provided by PolyOne Corporation

Physical Properties	Metric	English	Comments
Specific Gravity	1.75 g/cc	1.75 g/cc	ASTM D792
Water Absorption	0.030 % @Thickness 3.17 mm	0.030 % @Thickness 0.125 in	24 hr immersion; ASTM D570
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	54.5 MPa	7900 psi	Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
Elongation at Break	0.20 %	0.20 %	Type 1 - Rigids, 0.2 in/min; ASTM D638
Tensile Modulus	22.8 GPa	3300 ksi	Type 1 - Rigids, 0.2 in/min; ASTM D638
Flexural Strength	91.0 MPa	13200 psi	ASTM D790
Flexural Modulus	22.1 GPa	3200 ksi	ASTM D790
Izod Impact, Notched	0.160 J/cm @Thickness 6.35 mm, Temperature 23.0 °C	0.300 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F	Method A, Injection Molded; ASTM D256

Thermal Properties	Metric	English	Comments
Thermal Conductivity	4.01 - 5.00 W/m-K	27.8 - 34.7 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	282 °C	540 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	266 °C	510 °F	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 - 1.00e+16 ohm-cm	1.00e+15 - 1.00e+16 ohm-cm	ASTM D257
Surface Resistivity per Square	1.00e+13 - 1.00e+14 ohm	1.00e+13 - 1.00e+14 ohm	ASTM D257

Processing Properties	Metric	English	Comments
Melt Temperature	316 - 329 °C	600 - 625 °F	Molding
Mold Temperature	121 - 149 °C	250 - 300 °F