PolyOne Stat-Tech™ X ST6600-0040 ES FR Black Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ X ST6600-0040 ES FR Black Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.22 g/cc	1.22 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.017 - 0.018 cm/cm	0.017 - 0.018 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	169 MPa	24500 psi	ASTM D638
Elongation at Break	0.42 %	0.42 %	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	322 MPa	46700 psi	ASTM D790
Flexural Modulus	23.5 GPa	3410 ksi	ASTM D790
Izod Impact, Notched	0.690 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	1.29 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	>= 245 °C	>= 473 °F	Unannealed; ASTM D648
Flammability, UL94	V-0	V-0	Internal Method; UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	10 - 1000 ohm-cm	10 - 1000 ohm-cm	ASTM D257
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257
Static Decay	0.0020 sec	0.0020 sec	(Mil-B-81705C), 12% RH, 5000kV to 50kV
Shielding Effectiveness	42 dB @Frequency 1.00e+9 Hz	42 dB @Frequency 1.00e+9 Hz	1/8 thickness
	54 dB @Frequency 5.00e+9 Hz	54 dB @Frequency 5.00e+9 Hz	1/8 thickness
	68 dB @Frequency 1.00e+10 Hz	68 dB @Frequency 1.00e+10 Hz	1/8 thickness

Processing Properties	Metric	English	Comments
Drying Temperature	71.1 - 82.2 °C	160 - 180 °F

Descriptive Properties	Value	Comments
Features	Good Chemical Resistance
	High Stiffness
	Semi Crystalline
Filler / Reinforcement	Carbon Fiber Reinforcement, 40% Filler by Weight
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Aerospace Applications
	Business Equipment
	Computer Components
	Connectors
	Electrical/Electronic Applications