NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D792 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 16.0 MPa | 2320 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Elongation at Break, MD | 850 % | 850 % | ASTM D882 |
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 |
| Secant Modulus, MD | 0.280 GPa | 40.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.310 GPa | 45.0 ksi | ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 2.00 g/micron | 50.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 12.0 g/micron | 305 g/mil | ASTM D1922 |
| Dart Drop | 1.00 g/micron | 25.4 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % @Thickness 0.0250 mm |
3.0 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1007L Polycarbonate
- Petroquimica Triunfo Trithene® CX 7065 LDPE - Extrusion Coating
- Mitsui Fybrel® E 790 Polyolefin Synthetic Pulp, Wet Processes (discontinued **)
- Osprey Metals 17-4 PH Stainless Steel Powder (Grade 80% - 22)
- IDI Composites E-204 Thermoset Polyester, Sheet
- Dow Corning 2-1491 EMULSION
- BASF Novolen® 2348 M Polypropylene
- Teknor Apex APEX® 3201-75 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved