3D Systems Accura® accuGen™ Nd Plastic for SLA® Systems

Category	Polymer , Rapid Prototyping Polymer
Manufacturer	3D Systems Corporation
Trade Name	Accura®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3D Systems Accura® accuGen™ Nd Plastic for SLA® Systems.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Our most versatile material combines accuracy, green strength, and build chamber environment independence. For the SLA® Viper si2™, 3500, 5000 & 7000 systems.Typical ApplicationsMulti-purpose modelsRTV mold patternsForm/Fit/FunctionQuickCast™ patterns for investment castingMaster patterns for secondary processesPrototype toolingAll information provided by 3D Systems.

Physical Properties	Metric	English	Comments
Density	1.10 g/cc @Temperature 25.0 °C	0.0397 lb/in³ @Temperature 77.0 °F	Liquid
Viscosity	500 cP @Temperature 30.0 °C	500 cP @Temperature 86.0 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	82	82	90 Minute UV Cure; SLA 3500 System; ASTM D2240
Tensile Strength, Yield	67.0 MPa	9720 psi	90 Minute UV Cure; SLA 3500 System; ASTM D638
Elongation at Break	4.6 %	4.6 %	90 Minute UV Cure; SLA 3500 System; ASTM D638
Tensile Modulus	3.03 GPa	439 ksi	90 Minute UV Cure; SLA 3500 System; ASTM D638
Flexural Strength	79.0 MPa	11500 psi	90 Minute UV Cure; SLA 3500 System; ASTM D790
Flexural Modulus	1.93 GPa	280 ksi	ASTM D790
Izod Impact, Notched	0.171 J/cm	0.320 ft-lb/in	90 Minute UV Cure; SLA 3500 System; ASTM D256
Penetration	4.4	4.4	mils

Thermal Properties	Metric	English	Comments
CTE, linear	72.0 µm/m-°C	40.0 µin/in-°F	T<Tg; 90 Minute UV Cure; SLA 3500 System; ASTM E831-93
	176 µm/m-°C	97.8 µin/in-°F	T>Tg; 90 Minute UV Cure; SLA 3500 System; ASTM E831-93
Glass Transition Temp, Tg	73.0 °C	163 °F	90 Minute UV Cure; SLA 3500 System; DMA, E"

Descriptive Properties	Value	Comments
Critical Exposure (mJ/cm²)	10.8
Tested Build Styles	QuickCast, EXACT™, ThinLayer™ (NA on Viper si2 system), EXACTHR (Viper si2 system only)