PolyOne Stat-Tech™ AS-1000 AS Acrylonitrile Butadiene Styrene (ABS)

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ AS-1000 AS Acrylonitrile Butadiene Styrene (ABS).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.06 g/cc	1.06 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955
Melt Flow	8.5 g/10 min	8.5 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	35.0 MPa	5080 psi	ASTM D638
Elongation at Break	12 %	12 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	1.94 GPa	281 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	59.8 MPa	8670 psi	ASTM D790
Flexural Modulus	20.7 GPa	3000 ksi	ASTM D790
Izod Impact, Notched	2.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	3.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	87.0 °C @Thickness 6.35 mm	189 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	74.0 °C @Thickness 6.35 mm	165 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 - 1.00e+12 ohm-cm	1.00e+11 - 1.00e+12 ohm-cm	ASTM D257
Surface Resistance	1.00e+11 - 1.00e+12 ohm	1.00e+11 - 1.00e+12 ohm	ASTM D257
Static Decay	0.10 sec	0.10 sec	(Mil-B-81705C), 50% RH, 5000 kV to 50 kV
	0.30 sec	0.30 sec	(Mil-B-81705C), 12% RH, 5000 kV to 50 kV

Processing Properties	Metric	English	Comments
Melt Temperature	227 - 238 °C	441 - 460 °F

Descriptive Properties	Value	Comments
Features	Antistatic
	Non-Sloughing
Forms	Pellets
Generic Material	ABS
Generic Name	Acrylonitrile Butadiene Styrene (ABS)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Electrical Housing
	Electrical/Electronic Applications
	Housings